Lihlahisoa
Peroxide crosslinkable Semi-conductive shielding material for 35kV le ka tlase ho lithapo tsa XLPE
Kenyelletso ea Sehlahisoa
Sehlahisoa sena se sebetsa bakeng sa tšireletso ea conductor le mehala e kenelletseng ea 35kV le ka tlase ho XLPE e insulated. E entsoe ka thepa e tala e tsoang kantle ho naha ka lisebelisoa tsa extrusion tsa Swiss BUSS ka mokhoa oa ho kopanya. Bokaholimo ba likhoele bo boreleli.
Sesupo sa Tshebetso
Khothalletsa ho sebetsa le PE extruder
| Mohlala | Mocheso oa Moqomo oa Mochini | Molding Mocheso |
| OW-YP-35 | 70-115 ℃ | 110-117 ℃ |
Tekheniki Parameters
| No | Ntho | Yuniti | Litlhoko tsa Tekheniki |
| 1 | Relative Density | g/cm³ | ≤1.20 |
| 2 | Matla a tšepe | MPa | ≥12 |
| 3 | Elongation at Break | % | ≥240 |
| 4 | 20 ℃ Ho hanyetsa Bolumo | Ω·cm | ≤100 |
| 5 | 90 ℃ Ho hanyetsa Molumo | Ω·cm | ≤1000 |
| 6 | 90 ℃ Ho hanyetsa Bophahamo ka mor'a botsofali ba moea (100 ℃×168h) | Ω·cm | ≤1000 |
| 7 | Teko ea Botsofali ba Moea | / | (135±2℃)×168h |
| 8 | Phapang ea Matla a Tensile Ka mor'a Botsofali | % | ±25 |
| 9 | Phapang ea Elongation Ka mor'a Botsofali | % | ±25 |
| 10 | Hot Set Test | / | 200℃×0.2MPa×15mins |
| 11 | Elongation e chesang | % | ≤100 |
| 12 | Phetoho e sa Feleng ka mor'a ho Pholisa (Beha) | % | ≤15 |
| 13 | Matla a Peel 20 ℃ | N/cm | - |
| Tlhokomeliso: Lintlha tse ling, ka kopo ikopanye le basebetsi ba rona ba thekiso. | |||
-
70℃ Motsoako o Bonolo o sa Loteng oa Insulation
-
90℃ Motsoako oa Sheath oa Flame Retardant o se nang lead
-
90℃ Mofuta oa I oa Motsoako o se nang Loto oa Sheath
-
Insulation Material bakeng sa 10kV le ka tlase ho Silane X...
-
70℃ Motsoako oa Insulation oa Flame Retardant o se nang lead
-
90℃ Mofuta oa II oa Motsoako oa Sheath o se nang Loto
MELAO EA MAHALA MAHALA
LEFATŠE LE LE MONG le Ikemiseditse ho Fana ka Bareki ka terata ya boleng bo hodimo le disebediswa tsa thapo le ditshebeletso tsa First Classtechnical.
U ka Kopa Mohlala oa Mahala oa Sehlahisoa seo U se Thahasellang ho bolelang hore u ikemiselitse ho sebelisa sehlahisoa sa rona bakeng sa tlhahiso.
Re Sebelisa Feela Lintlha tsa Teko tseo u ikemiselitseng ho li araba le ho li arolelana joalo ka netefatso ea litšoaneleho le boleng ba sehlahisoa, 'me u re thuse ho theha Sistimi e Felletseng ea Taolo ea Boleng ho Ntlafatsa Tšepo ea Bareki le Boikemisetso ba ho Reka.
U ka Tlatsa Foromo e Ka Ho Le letona Ho Kopa Sample ea Mahala
Litaelo tsa Tšebeliso
1 . Moreki o na le Account ea International Express Delivery Account ka boithatelo o lefa Thepa ( Thepa e ka khutlisetsoa ka Odara)
2 . Setsi se Tšoanang se ka Etsa Kopo Feela Bakeng sa Mohlala o le Mong oa Mahala oa Sehlahisoa se Tšoanang, 'me Setsi se Sona se ka Etsa Kopo Bakeng sa Mesampole e Mehlano ea Lihlahisoa tse Fapaneng Mahala Pele Selemo se le seng.
3 . Mohlala ke oa bareki ba fektheri ea terata le ea lithapo feela, 'me ke feela bakeng sa basebetsi ba laboratori bakeng sa tlhahlobo ea tlhahiso kapa lipatlisiso.
MOHLALA PAKA
MOSEBETSI OA KOPO EA MAHALA
Ka kopo, Kenya Litlhaloso tsa Mohlala tse Hlokehang, Kapa Hlalosa ka bokhuts'oane Litlhoko tsa Morero, re tla u khothaletsa lisampole.
Kamora ho fana ka foromo, tlhahisoleseling eo u e tlatsitseng e ka fetisetsoa ho ONE WORLD background bakeng sa ts'ebetso e eketsehileng ho fumana lintlha tsa sehlahisoa le lintlha tsa aterese le uena. Hape o ka ikopanya le uena ka mohala. Ke kopa o bale ea ronaleano la lekunutuBakeng sa lintlha tse ling.