Motsoako oa PA12
Kenyelletso ea Sehlahisoa
PA12 Compound e loketse ho kenya kapa ho roala lithapo tsa motlakase le likhoele. Sehlahisoa se na le li-plasticizers 'me se na le botsitso ba mocheso le botsitso ba UV. Sehlahisoa se lumellana le litekanyetso tsa RoHS le REACH.
Sesupo sa Tshebetso
| Mocheso pele ho omisa | nako ea pele ho ho omisa | extrusion mocheso |
| 80-110 ℃ | 4–6 h | 210-260 ℃ |
Lintlha tse tloaelehileng tse boletsoeng ka holimo li fanoe bakeng sa litšupiso tsa mosebedisi. Ts'ebetsong ea 'nete ea tlhahiso le ts'ebeliso, liphetoho tsa ts'ebetso li ka etsoa ho latela sehlahisoa se ikhethileng se etsoang. Bakeng sa mekhoa e tsoelang pele ea tlhahiso, ho kgothaletswa ho sebelisa lisebelisoa tsa ho omisa ka mokhoa o tsitsitseng, 'me mocheso o khothalletsoang oa ho omisa o oela ka har'a mocheso oa mocheso pele ho omisa.
Tekheniki Parameters
| Che. | Ntho | Boemo ba Teko | Yuniti | Lintlha tse tloaelehileng |
| 1 | Matla a Kobehang | 2mm/mots | Mpa | 36 |
| 2 | Ho Kobeha Modulus | Mpa | 950 | |
| 3 | Matla a tšepe | 50mm/mots | Mpa | 45 |
| 4 | Tensile Elongation nakong ea Phomolo | % | ≥200 | |
| 5 | Charpy Impact Strength (Beam e Tšehetsoeng Feela e Notched) | 23 ℃ | kJ/m2 | 65 |
| -30 ℃ | 24 | |||
| 6 | Bothata ba Lebopo | D,15s | Shore D | 74 |
| 7 | Melting Point | DSC | 179 | |
| 8 | Mocheso oa ho Fetola Mocheso | 1.8MPa | ℃ | 45 |
| 0.45MPa | ℃ | 85 | ||
| 9 | Mophato wa Kganyetsano ya Lelakabe (0.8mm) | - | Lintlha | HB |
| 10 | Ho hanyetsa Molumo | - | Ω·m | ≥1010 |
| 11 | Bokaholimo ba Resistivity | - | Ω | ≥1010 |
| 12 | Relative Tracking Index | - | - | 600 |
| 13 | Botenya | 23 ℃ | g/cm3 | 1.0 |
MELAO EA MAHALA MAHALA
LEFATŠE LE LE MONG le Ikemiseditse ho Fana ka Bareki ka terata ya boleng bo hodimo le disebediswa tsa thapo le ditshebeletso tsa First Classtechnical.
U ka Kopa Mohlala oa Mahala oa Sehlahisoa seo U se Thahasellang ho bolelang hore u ikemiselitse ho sebelisa sehlahisoa sa rona bakeng sa tlhahiso.
Re Sebelisa Feela Lintlha tsa Teko tseo u ikemiselitseng ho li araba le ho li arolelana joalo ka netefatso ea litšoaneleho le boleng ba sehlahisoa, 'me u re thuse ho theha Sistimi e Felletseng ea Taolo ea Boleng ho Ntlafatsa Tšepo ea Bareki le Boikemisetso ba ho Reka.
U ka Tlatsa Foromo e Ka Ho Le letona Ho Kopa Sample ea Mahala
Litaelo tsa Tšebeliso
1 . Moreki o na le Account ea International Express Delivery Account ka boithatelo o lefa Thepa ( Thepa e ka khutlisetsoa ka Odara)
2 . Setsi se Tšoanang se ka Etsa Kopo Feela Bakeng sa Mohlala o le Mong oa Mahala oa Sehlahisoa se Tšoanang, 'me Setsi se Sona se ka Etsa Kopo Bakeng sa Mesampole e Mehlano ea Lihlahisoa tse Fapaneng Mahala Pele Selemo se le seng.
3 . Mohlala ke oa bareki ba fektheri ea terata le ea lithapo feela, 'me ke feela bakeng sa basebetsi ba laboratori bakeng sa tlhahlobo ea tlhahiso kapa lipatlisiso.
MOHLALA PAKA
MOSEBETSI OA KOPO EA MAHALA
Ka kopo, Kenya Litlhaloso tsa Mohlala tse Hlokehang, Kapa Hlalosa ka bokhuts'oane Litlhoko tsa Morero, re tla u khothaletsa lisampole.
Kamora ho fana ka foromo, tlhahisoleseling eo u e tlatsitseng e ka fetisetsoa ho ONE WORLD background bakeng sa ts'ebetso e eketsehileng ho fumana lintlha tsa sehlahisoa le lintlha tsa aterese le uena. Hape o ka ikopanya le uena ka mohala. Ke kopa o bale ea ronaleano la lekunutuBakeng sa lintlha tse ling.