Insulation Material bakeng sa 10kV le ka tlase ho Silane XLPE Aerial Cables
Kenyelletso ea Sehlahisoa
Sehlahisoa ke methati e 'meli ea silane cross-linkable polyethylene insulation compounds. E sebelisoa haholo-holo bakeng sa ho kenya likhoele tse kaholimo ho li-voltage tse tlase-tlase ka ts'ebetso ea tlhahiso ea hlobo ea squeeze tube. Lithapo tse sebetsang ka matla ke 10kV mme ka tlase, mocheso o phahameng ka ho fetisisa o sebetsang ke 90 ℃. 'Mala oa sehlahisoa sena o ntšo haeba ho se na litlhaloso tse khethehileng.
Sesupo sa Tshebetso
Khothalletsa ho sebetsa le PE extruder
| Mohlala | Mocheso oa Moqomo oa Mochini | Molding Mocheso |
| OW-YJG(2)K-10 | 155-175 ℃ | 180-190 ℃ |
Tekheniki Parameters
| Che. | Ntho | Yuniti | Litlhoko tsa Tekheniki | ||
| 1 | Botenya | g/cm³ | 0.922±0.005 | ||
| 2 | Matla a tšepe | MPa | ≥13.0 | ||
| 3 | Elongation at Break | % | ≥300 | ||
| 4 | Brittle Mocheso ka Mocheso o Tlase | ℃ Ho hloleha Rate | -76 ≤15/30 | ||
| 5 | 20 ℃ Ts'ebetso ea ho hanyetsa Bolumo | Ω·m | ≥1.0×10¹⁴ | ||
| 6 | 20 ℃ Matla a Dielectric, 50Hz | MV/m | ≥25.0 | ||
| 7 | 20 ℃ Dielectric Constant, 50Hz | % | ≤2.35 | ||
| 8 | Boemo ba Botsofali ba Moea 135±2℃×168h | Phapang ea Matla a Tensile Ka mor'a Botsofali | % | ±20 | |
| Phapang ea Elongation Ka mor'a Botsofali | % | ±20 | |||
| 9 | Botsofali ba Boemo ba Leholimo ba Maiketsetso | Phapang ea Matla a Tensile Ka mor'a Botsofali | % | ±30 | |
| Phapang ea Elongation Ka mor'a Botsofali | % | ±30 | |||
| 10 | Botsofali ba Boemo ba Leholimo ba Maiketsetso | Phapang ea Matla a Tensile Ka mor'a Botsofali | % | ±30 | |
| Phapang ea Elongation Ka mor'a Botsofali | % | ±30 | |||
| 11 | Hot Set Test Condition 200×0.2MPa×15min | 1mm botenya 95 ℃ phehiloeng 2 lihora teko | Elongation e chesang | % | ≤100 |
| Phetoho e sa feleng ka mor'a Cooling | % | ≤5 | |||
| Tlhokomeliso: Lintlha tse ling, ka kopo ikopanye le basebetsi ba rona ba thekiso. | |||||
MELAO EA MAHALA MAHALA
LEFATŠE LE LE MONG le Ikemiseditse ho Fana ka Bareki ka terata ya boleng bo hodimo le disebediswa tsa thapo le ditshebeletso tsa First Classtechnical.
U ka Kopa Mohlala oa Mahala oa Sehlahisoa seo U se Thahasellang ho bolelang hore u ikemiselitse ho sebelisa sehlahisoa sa rona bakeng sa tlhahiso.
Re Sebelisa Feela Lintlha tsa Teko tseo u ikemiselitseng ho li araba le ho li arolelana joalo ka netefatso ea litšoaneleho le boleng ba sehlahisoa, 'me u re thuse ho theha Sistimi e Felletseng ea Taolo ea Boleng ho Ntlafatsa Tšepo ea Bareki le Boikemisetso ba ho Reka.
U ka Tlatsa Foromo e Ka Ho Le letona Ho Kopa Sample ea Mahala
Litaelo tsa Tšebeliso
1 . Moreki o na le Account ea International Express Delivery Account ka boithatelo o lefa Thepa ( Thepa e ka khutlisetsoa ka Odara)
2 . Setsi se Tšoanang se ka Etsa Kopo Feela Bakeng sa Mohlala o le Mong oa Mahala oa Sehlahisoa se Tšoanang, 'me Setsi se Sona se ka Etsa Kopo Bakeng sa Mesampole e Mehlano ea Lihlahisoa tse Fapaneng Mahala Pele Selemo se le seng.
3 . Mohlala ke oa bareki ba fektheri ea terata le ea lithapo feela, 'me ke feela bakeng sa basebetsi ba laboratori bakeng sa tlhahlobo ea tlhahiso kapa lipatlisiso.
MOHLALA PAKA
MOSEBETSI OA KOPO EA MAHALA
Ka kopo, Kenya Litlhaloso tsa Mohlala tse Hlokehang, Kapa Hlalosa ka bokhuts'oane Litlhoko tsa Morero, re tla u khothaletsa lisampole.
Kamora ho fana ka foromo, tlhahisoleseling eo u e tlatsitseng e ka fetisetsoa ho ONE WORLD background bakeng sa ts'ebetso e eketsehileng ho fumana lintlha tsa sehlahisoa le lintlha tsa aterese le uena. Hape o ka ikopanya le uena ka mohala. Ke kopa o bale ea ronaleano la lekunutuBakeng sa lintlha tse ling.